摘要：介绍聚酰亚胺纤维一步法生产线流程，对实际生产中出现的成品丝束含水量大的问题，针对涉及的设备装置进行分析探讨，提出更改方案。对卷曲前方案考虑增加烘干定型机组所属橡胶轧辊的气源压力，提高卷曲系统的电加热温度；对卷曲后方案考虑将浸泡式上油改为摩擦式上油，延长丝束热定型时间，达到降低丝束含水量的目的。指出，调节橡胶轧辊的气源压力和增加电加热设备工作温度的方案简单易操作，达到使用要求。
关  键  词：聚酰亚胺；纤维性能；含水量；后处理；卷曲
中图分类号：TS102.52⁺1      文献标志码：B      文章编号：1001-9634(2014)03-0043-02
  Abstract:Introduction is made to the one-step production flow of polyimide fiber,As to the high water content in the fiber tow,solution is given to the problem through modification of the equipment involved.The air pressure increases for rubber roller on the hot setting equipment before the crimping process,and the electric heating temperature is also increased for crimping system.As to the after crimping process,it is better to use friction oiler instead of tension oiler,so as to increase the hot setting time of the tow fiber,consequently,the water content in the fiber tow reduced.Conclusion is made that regulation of the air pressure plus the increase of the hot setting temperature is a simple solution to the problem as desired.
Key Words:polyimide fiber;fiber performance;water content;after-treatment; crimping
 
收稿日期：2013-07-11
作者简介：元士磊（1983—），男，河北沙河人，工程师，主要从事化纤机械设计方面的研究。
参考文献：
[1]元士磊.特种纤维生产线上短纤维卷曲机的设计改进[J].纺织器材,2012，39(1)：24-26.
[2]元士磊.浅谈短纤维卷曲机密封侧板的设计[J].国际纺织导报,2011，39(4)：59-60.
[3]元士磊，荆旭东，侯振奎.甲壳素类纤维湿法纺成套设备的研究与探讨[J].国际纺织导报,2012，40(1):50-51.
[4]王曙中，王庆瑞，刘兆峰.高科技纤维概论[M].上海：中国纺织大学出版社，1998. 55-156.
[5]高占勇.PAN基碳纤维原丝生产线的研发[J].高科技纤维与应用，2011，36(5):39-41.

http://www.ctainfo.cn/uploadfile/2015/0305/20150305094116755.pdf