聚氨酯细纱胶辊的应用与研究
2017-06-07 16:59:48   来源：   评论：0 点击：

   
摘要：为了提高细纱成纱质量，介绍了聚氨酯弹性体材料的特点，详细对比分析了不同硬度、不同厂家聚氨酯胶辊与丁腈胶辊在不同工艺应用不同器材后的试纺对比，从套制、磨砺、表面处理和回磨周期四个方面探讨了如何对聚氨酯胶辊进行正确使用与维护。指出：聚氨酯胶辊能明显降低成纱粗节、细节和棉结，在使用中变形极小且耐用，上车基本无走熟期，能适应车间温湿度的突然变化；生产使用中，聚氨酯胶辊硬度可偏低选择，具有较长的上机使用周期，涩性较强，易粘带纤维，须加强维护管理，做好磨砺和表面处理，保持胶辊表面细腻、滑爽。
关键词：聚氨酯胶辊；丁腈胶辊；硬度；成纱质量；摇架压力；磨砺；套制；弹性；笔涂处理
中图分类号：TS103.82⁺3  文献标志码：B  文章编号：1001-9634(2017)03-0038-05
   
Abstract: To improve the spinning quality of yarn，introduction is made to the characteristics of PU elastomer material.Detailed comparative analysis is done to rollers of different hardness,different manufacturers and NBR rollers in different process using different accessories in trial spinning.Probing is done into the cautions in correct use and maintenance of PU rollers from telescoping,grinding,surface treatment and regrinding.It is pointed out that PU rollers can significantly reduce nubs,thins,and neps.The rollers are of small deformation and good durability.There is no phase-in period,adapt to sudden changes in humiture in production.It is recommended that Pu rollers can be selected in a lower degree than that as desired.However,the Pu rollers have long service cycle with strong astringent,easy stick with fiber.Something must be done to strengthen maintenance management,grinding surface treatment,keeping the roller surface smooth.
Key Words: Polyurethane cots;NBR rollers;hardness;yarn quality;cradle pressure;grinding;telescping;elasticity;brush coating treatment
 
收稿日期： 2016-08-06
作者简介：吉宜军(1966—)，男，江苏海安人，高级工程师，主要从事纺纱技术研究、产品开发和生产管理等方面的工作。
网络出版时间： 2016-10-08  21:21
http://www.cnki.net/kcms/detail/61.1131.TS.20161008.2121.080.html
 
参考文献：
［1］ 余桂林.聚氨酯胶辊的特性与应用［J］.棉纺织技术，2012，40（11）：1-5．
［2］ 唐文辉，倪士敏.高弹性低硬度胶辊应用技术探讨［J］.棉纺织技术，2004，32（12）：29-31．
［3］ 唐文辉.胶辊胶圈的技术进步与发展［C］//“五爱·潜阳杯”2014’纺织器材制造、应用及新技术交流研讨会论文集.咸阳：全国纺织器材科技信息中心，2014：87-100.
［4］ 任守平，傅霜豫.胶辊压力与纺纱质量的关系［J］.棉纺织技术，2000，28（11）：16-18．

http://www.ctainfo.cn/uploadfile/2017/0621/20170621060245293.pdf